Home Page | CollectionWelcome to TKD CO., LTD

TKD CO., LTD

Home > News > Technical Knowledge > Research on PCD vacuum brazing technology

News

Company News
Warmly congratulation! T…
PKD-Werkzeuge zum Lasersc…
La macchina per il taglio…
Die neue Generation Fiber…
The new generation of PKD…
Soluzioni di taglio altam…
PKD PCD CBN Diamantfaser-…
Ceramic Fiber Laser Cutti…
New Fiber Laser Drilling …
Vacuum brazing oven furna…
Industry News
Detailed explanation of l…
Major breakthrough! China…
Henan company made its de…
Application and developme…
Powerphotonics Releases N…
Research on 2035 developm…
IPG Q3 profits increase b…
The superhard material cu…
Fiber laser leads into th…
The international standar…
Technical Knowledge
One article to understand…
PKD-Schleifeigenschaften …
One article to understand…
Laser-Cutting PCD Tools
Centennial history of las…
Centennial history of las…
Centennial history of las…
Interpretation and sel…
Interpretation and sel…
Laser Roughing of PCD

Research on PCD vacuum brazing technology

2020/12/3 15:33:46 TKD CO., LTD Reading 98 Times

PCD PCBN Vacuum brazing oven furnace 2.jpg

The brazing technology is indispensable in the application of PCD compact. Vacuum brazing has the advantages of accurate brazing temperature, uniform heating, many brazing points at the same time, no surface treatment after brazing and so on. The size of the cutting tool product for vacuum brazing should not be too large and must be able to be put into the vacuum furnace. At the same time, the tool material must be able to withstand the temperature change during the brazing process and maintain its own performance. Vacuum brazing process is especially suitable for mass-produced PCD cutting tools with small size and can be heated as a whole, and it can braze multiple points at a time, but it is not suitable for PCD product with larger size or that can only accept local heating.

For PCD cutting tool products, vacuum brazing process can be divided into preparation work before entering the furnace and vacuum brazing process in the furnace. Preparation: For PCD tool products to be vacuum brazed, select appropriate vacuum solder (usually solder paste) and apply it correctly to the insert groove, then place the insert in a fixed position to be cured by solder paste; furnace: Put the processed PCD cutting tool products into a vacuum furnace, seal and vacuum continuously, and then heat, melt solder, complete brazing action, cool and get out of the furnace according to the procedure in vacuum. The purpose of vacuum brazing is to make the molten solder evenly distributed to all parts of the brazing seam under the action of capillary pipette, so as to achieve the ideal brazing effect.

(I)The factors affecting the preparation of vacuum brazing are shown in Table 1.

TABLE 1.png

(II)Technological conditions

When the temperature is below the solidus, the solder itself is relatively stable, and there will be no softening, modification and other problems; when the temperature is higher than the liquidus, the solder will completely melt and maintain the properties of the alloy; but when the temperature is between the solidus and the liquidus, if the time is not long, the solder is only in the softening or partial melting state, and there will be no qualitative change; if it is in this temperature range for a long time, segregation will occur. Once the segregation occurs, the performance of the solder will change, which will affect the brazing effect. Therefore, in the brazing process, it is necessary to quickly raise the temperature from the solidus to above the liquidus, so as to prevent the possibility of segregation of solder, so as to better ensure the stability of brazing quality. The process conditions are shown in Table 2.

Table 2

TABLE2.png

In a specific temperature range, the wettability of the solder is proportional to the brazing temperature; at the same brazing temperature, the brazing strength increases at first and then decreases with the extension of holding time; the flow blocker is suitable for products with high appearance requirements, it can effectively prevent the solder from adhering to the non-brazed surface.

To sum up, for PCD cutting tools, vacuum brazing process can effectively eliminate the influence of air on PCD and keep a good appearance of cutters. The heating temperature in the vacuum furnace is uniform, the deformation of the product is small, and the tool is not easy to crack. Under the condition of stable process, the product quality of each furnace is consistent, which is especially suitable for mass production of small size PCD cutting tools.


Pre: High Quality Vacuum Brazing Furnace For PCD PCBN Diamond tools making
Next: Application of vacuum brazing technology
2010-2023 all right reserved © TKD CO., LTD Home | About US | Contact Us | Contact Us | Face Book | SiteMap | 豫ICP备18018494号